| abstract |
(57) [Summary] [Structure] 0.001 to 30 parts by weight of an organic peroxide and 100% by weight of a thermoplastic hydrogenated ring-opening norbornene-based resin (preferably a hydrogenation rate of 90% or more), and a crosslinking aid. (Preferably allyl-based crosslinking agent or methacrylate-based crosslinking aid) is added in an amount of 0.1 to 1 with respect to 1 part by weight of organic peroxide. 0 parts by weight, preferably a resin 1 containing a flame retardant having a specific structure Add 5 to 150 parts by weight to 00 parts by weight to obtain a uniformly dispersed crosslinkable norbornene-based resin composition, and form into a film or prepreg, laminate, heat compression mold and crosslink / heat fuse To obtain a crosslinked molded article. [Effect] A cross-linked molded product having excellent heat resistance, chemical resistance, moisture resistance, water resistance, and electrical characteristics and having no unevenness can be obtained. |