| abstract |
A curable particulate silicone composition which has a hot melt property, is excellent in handling workability and curing property, has a high light reflectance in a visible wavelength range, and provides a cured product having excellent flexibility and toughness at a high temperature from room temperature to about 150 ° C And uses thereof. (A) hot melt silicone fine particles having a softening point of 30 ° C or higher and having a hydrosilylation reactive group and / or a radical reactive group, (B) an inorganic filler substantially containing no coarse particles having an average particle diameter of 5 μm or more, , And (C) a curing agent and has a storage elastic modulus at 25 占 폚 and 150 占 폚 of not more than 2000 MPa and not more than 100 MPa by curing, a wavelength of 450 nm at a thickness of 100 占 퐉, very suitably 700 lt; RTI ID = 0.0 > nm / nm < / RTI > |