abstract |
A curable particulate silicone composition which has a hot melt property, is excellent in handling workability and curing property, is excellent in gap filling property at the time of melting, and provides a cured product excellent in flexibility and toughness at a high temperature from room temperature to about 150 ° C, And a pellet formed by molding a curable granular silicone composition. (A) hot melt silicone fine particles having a softening point of 30 ° C or higher and having a hydrosilylation reactive group and / or a radical reactive group, (B) an inorganic filler substantially containing no coarse particles having an average particle diameter of 10.0 탆 or more, And a curing agent (C), wherein the curing agent has a storage elastic modulus at 25 占 폚 and 150 占 폚, respectively, of 2000 MPa or less and 100 MPa or less by curing, And uses thereof. |