http://rdf.ncbi.nlm.nih.gov/pubchem/patent/KR-101316154-B1
Outgoing Links
Predicate | Object |
---|---|
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C23C14-06 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C22C38-02 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C23C14-35 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C22C38-04 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C23C14-06 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C23C14-35 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C38-00 |
filingDate | 2012-02-29-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2013-10-08-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2013-10-08-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | KR-101316154-B1 |
titleOfInvention | High carbon steel wire for strong core aluminum stranded wire with excellent electrical conductivity and manufacturing method thereof |
abstract | Preparing a high-strength steel wire for aluminum core wire having excellent electrical conductivity, comprising the step of preparing a steel wire without an aluminum-zinc plated layer, and forming a coating layer of titanium nitride having a thickness of 10 ~ 15㎛ on the surface of the steel wire A manufacturing method and a steel wire produced by the method are provided. According to the present invention, it is possible to provide a high carbon steel wire for ACSR having excellent electrical conductivity without using expensive Ni almost. |
priorityDate | 2012-02-29-04:00^^<http://www.w3.org/2001/XMLSchema#date> |