| abstract |
PURPOSE: To obtain a nylon 46 resin composition having remarkably improved moldability while keeping the excellent characteristics of nylon 46 resin, by compounding a specific amount of a phenoxy resin to a nylon 46 resin. n CONSTITUTION: (A) 100pts.wt. of a nylon 46 resin produced by condensation reaction of adipic acid (derivative) as acid component and tetramethylenediamine (derivative) as amine component and having an intrinsic viscosity of preferably 0.8W2, especially 1.3W1.7 (measured in m-cresol at 35°C) is compounded with (B) 1W100pts.wt. of a phenoxy resin having an average molecular weight of 10,000W100,000 and synthesized from 2,2-bis(4-hydroxyphenyl)propane and epichlorohydrin and, if necessary, (C) other compounding components. The obtained mixture is uniformly mixed e.g. with a blender to obtain the objective composition. n COPYRIGHT: (C)1988,JPO&Japio |