| abstract |
(57) [Summary] [PROBLEMS] By using only a halogen-free flame retardant in metallocene LLDPE, a thin molded article such as a film can have sufficient flame retardancy, and a feeling similar to that of polyvinyl chloride resin. (No roughness) and no problem in mechanical strength and surface whitening resistance Provided is a flame-retardant resin composition which does not generate dioxin during combustion and a molded article thereof. SOLUTION: The metallocene LLDPE is 70 100 parts by weight of a synthetic resin containing 100 to 100% by weight, and BE Magnesium hydroxide 20 to 100 having a T specific surface area of 20 m 2 / g or less, an average secondary particle diameter measured by a laser diffraction scattering method of 5 μm or less, and a water-soluble sodium salt content of 500 ppm or less in terms of sodium. Parts by weight, 1 to 20 parts by weight of red phosphorus having an average secondary particle diameter of 30 μm or less, and 0.1 to 20 parts by weight of carbon powder, and the total of magnesium hydroxide, red phosphorus and carbon powder is 120 parts by weight. A flame-retardant resin composition characterized by the following, and a molded article thereof. |