| abstract |
A method for the production of a dye scavening substrate which comprises the steps of: (a) providing a cellulosic substrate; (b) passing the substrate through a bath containing an alkaline solution of an N-trisubstituted ammonium 2-hydroxy-3-halopropyl compound having general formula (I) or a salt of epoxy propyl ammonium having general formula (II), wherein X is a halogen radical, Y is a chloride, bromide, sulfate or sulfonate, and the R's are methyl, ethyl, butyl or benzyl groups or an hydroxyl substituted derivative thereof; (c) subjecting the substrate to a pressure of between 0.69 - 1.37MPa (100-200 psi); (d) heating the substrate to a temperature of approximately 35 °C; (e) wrapping the substrate in a water impermeable material and rotating the material at a temperature of between 15 °C and 100 °C for a period of between 1 hour and 12 hours; (f) removing the water impermeable material and passing the substrate through an acid bath; (g) subjecting the substrate to a pressure of between 1.03 - 1.72MPa (150-250 psi); and (h) drying the substrate. |