| abstract |
Provided is a method for forming a dry coating film on the surface of an object to be coated, the method including: a step for setting a dry coating film thickness T of 300 μm or higher; a step for preparing or using a colored coating that contains at least a binder resin and a colored pigment, the colored coating satisfying the conditions that (a) a flaky pigment having an average particle size of 10-300 μm, an average thickness of 2-50 μm, and an aspect ratio of 2-100 is also contained, (b) the flaky-pigment content is 5-45 vol% in the coating film-forming component, (c) a coating film having a film thickness T covers the surface, and (d) the color difference between a coating film of film thickness T and a coating film of film thickness 0.7T is 2.0 or greater; and a step for applying the colored coating until the surface is covered. Also provided is a coating used in this method. |