| abstract |
A solvent resistant, transparent aromatic polyamide film with a high refractive index may be made by reacting at least one aromatic diacid chloride, a first aromatic diamine, and at least one crosslinking agent or a second aromatic diamine in an organic solvent to form an aromatic polyamide polymer in solution. In one embodiment, the at least one aromatic diacid chloride is selected from the group consisting of isophthaloyl dichloride, terephthaloyl dichloride, 2, 6- naphthalene-dicarboxylic chloride, or combinations thereof and the first aromatic diamine is selected from the group consisting of 9, 9-Bis(4-hydroxyphenyl)fluorine, 2, 2 ',5,5'- Tetrachlorobenzidine, or combinations thereof. The organic solvent is then evaporated from the aromatic polyamide polymer in solution to form a transparent aromatic polyamide precursor film. The precursor film is then heated at a temperature close to the glass transition temperature of the transparent aromatic polyamide precursor film to form the solvent resistant, transparent aromatic polyamide film. |