| abstract |
The present invention relates to a method for joining two or more components made of glass, ceramic, and/or glass ceramic, using a soluble glass joining solution having sodium, potassium, and/or lithium ions and/or a silica sol, the joining solution being applied to joint surfaces between the components to be joined and solidified at mild temperatures, the method being either characterized in that the joining solution comprises an additive selected among boric acid, boron compounds from which boric acid can result by hydrolysis, aluminum acetates, aluminum silicate/NH3 /H2O titanium compounds forming titanium hydroxy cations, water-soluble zinc compounds, water-soluble zircon compounds, and water-soluble yttrium compounds, wherein said additive is added in an amount that reduces the pH value of the underlying soluble glass, and/or characterized in that, after the joining solution is applied and the components to be joined are brought together and fixed, the joined components are dried by removing water at room temperature, wherein, after drying, the joined components are tempered in vacuum at a temperature in the range of up to 200°C above room temperature. |