A polyester resin composition having an equivalent spherical diameter of 1 mm to 50 mm, a degree of crystallization of not less than 65% and less than 99%, an intrinsic viscosity of not more than 0.7 dl/g and a cyclic trimer content of not more than 0.4% by weight. This polyester resin composition has an excellent color tone, causes no significant viscosity lowering or viscosity rise, and can withstand a process which is exposed to a long-term heat history. A polyester resin composition having a viscosity suitable for extrusion in a general-purpose manner, a production process thereof, and a polyester film are also provided. |