| abstract |
A silicon nitride substrate including a phase encompassed of silicon nitride particles, and intergranular phase formed from a sintering aid, wherein a separation layer is formed on the surface of a molded body including silicon nitride powder, sintering aid powder, and organic binder, by using a boron nitride paste containing boron nitride powder, organic binder, and organic solvent; the separation layer and molded body are heated; the organic binder is removed from the separation layer and molded body; subsequently molded bodies stacked with a separation layer therebetween, are sintered. Boron nitride paste contains 0.01 to 0.50% by oxygen mass and 0.001 to 0.5% by carbon mass, and c/a is within range of 0.02 to 10.00, where c is oxygen content in the powder of the boron nitride paste, and a carbon content in the degreased separation layer, which includes 0.2 to 3.5 mg/cm 2 of hexagonal boron nitride powder. |