| abstract |
A ceramic sheet is produced by a method in which inorganic particles including, as a main component, an oxide represented by general formula ABO 3 and containing a volatile component are mixed such that the A/B ratio is 1.05 or more, the inorganic particles are formed into a self-supported planar shaped body with a thickness of 30 μm or less, and the shaped body is fired, without an inactive layer or with an inactive layer which does not substantially react with the shaped body and is disposed adjacent to the shaped body, at a temperature-rising rate of 30° C./min or more in a temperature range which is equal to or higher than a temperature at which the volatile component is volatilized. |