| abstract |
The present disclosure is directed to a base film having a thickness from 8 to 152 microns, a 60 degree gloss value from 2 to 35, an optical density greater than or equal to 2 and a dielectric strength greater than 1400 V/mil. The base film comprises a chemically converted (partially or wholly aromatic) polyimide in an amount from 71 to 96 weight percent of the base film. The base film further comprises a pigment and a matting agent. The matting agent is present in an amount from 1.6 to 10 weight percent of the base film, has a median particle size from 1.3 to 10 microns, and has a density from 2 to 4.5 g/cc. The pigment is present in an amount from 2 to 9 weight percent of the base film. The present disclosure is also directed to coverlay films comprising the base film in combination with an adhesive layer. |