| abstract |
A method for producing a flame retarding polypropylene fiber having both good flame retardancy and good fiber strength, and which generates no toxic gas, includes mixing 0.4% by wt. or more of a hindered amine-based stabilizer and 0.5% by wt. or more of a phosphoric ester-based flame retardant with a polypropylene resin having an MPR of 5 to 50 g/10 min, melt-spinning the mixture to form an undrawn yarn, drafting the yarn at a drafting magnification of 2 to 7 fold and a drafting temperature of 50 to 100° C., and further thermally setting at 60 to 140° C. |