| abstract |
A foam rubber composition and a method for making same which is foamable to a high degree and a molded product made from the foam rubber composition wherein the compositions has: (A) a low-molecular Ethylene-propylene-5-ethylidene-2-norbornene terpolymer having a Mooney viscosity (ML1+4 at 100 DEG C.) of 20 to 40, an ethylene/propylene ratio by weight of 65/35 to 50/50, an iodine value of 20 to 30, and a Q value (Mw/Mn) not exceeding 3 as determined by gel permeation chromatography; (B) a high-molecular ethylene-propylene-5-ethylidene-2-norbornene terpolymer having a Mooney viscosity (ML1+4 at 100 DEG C.) of 100 to 300, an ethylene/propylene ratio by weight of 65/35 to 50/50, an iodine value of 20 to 30 and a Q value (Mw/Mn) of 6 to 10; (C) a vulcanizing system agent containing sulfur as a vulcanizer, and zinc carbamate and sulfenamide as accelerators; and (D) a foaming agent containing N, N'-dinitrosopentamethylenetetramine and urea. |