| abstract |
Hollow polyester fibers having a thickness of 0.11 to 8.89 d tex (0.1 to 8.0 denier), a hollow volume (a cross-sectional area ratio of hollow to fiber) of 40 to 85%, and a crystallization degree of 20% or more and crystal size in (0 1 0) plane of 4 nm or more of polyester, has a high resistance to compression and a high recovery from compression and are useful for producing woven and knitted fabric having a high durability, pile sheet materials having high resistance to and recovery from pile prostration, and nonwoven fabrics and artificial leather materials having a high resistance and recovery from compression. |