| abstract |
Hydrophilic polyurethane foams with rapid wet out properties are formed from the reaction product of an MDI-based or polymeric MDI-based isocyanate capped prepolymer with an aqueous component, such as water, and about 0.5 to 2.0 parts by weight, based on 100 parts by weight prepolymer, of a silicone glycol copolymer liquid surfactant with a polyether portion, said surfactant having a viscosity of about 175 to 350 CST at 25 DEG C., a molecular weight in the range of about 1500 to 20,000, with the polyether portion having a molecular weight in the range of about 200 to 2000 and containing about 40 to 100 percent by weight ethylene oxide. The surface of the hydrophilic foam wets out or absorbs droplets of water in less than thirty (30) seconds, preferably instantaneously (less than one second). |