| abstract |
In accordance with the present invention, there are provided ethylene copolymers composed of structural units (a) derived from ethylene and structural units (b) derived from alpha -olefin of 3 DIFFERENCE 20 carbon atoms, said ethylene copolymers having [A] density of 0.85 DIFFERENCE 0.92 g/cm3, [B] an intrinsic viscosity [ eta ] as measured in decalin at 135 DEG C. of 0.1 DIFFERENCE 10 dl/g, [C] a ratio ( &upbar& Mw/ &upbar& Mn) of a weight average molecular weight ( &upbar& Mw) to a number average molecular weight ( &upbar& Mn) as measured by GPC of 1.2 DIFFERENCE 4, and [D] a ratio (MFR10/MFR2) of MFR10 under a load of 10 kg to MFR2 under a load of 2.16 kg at 190 DEG C. of 8 DIFFERENCE 50, and being narrow in molecular weight distribution and excellent in flowability. |