| abstract |
A thermoplastic resin composition having a good balance among rigidity, impact strength and adhesion of coating is provided, which comprises: a total of 100 parts by weight of (a)-(c) wherein (a) is 1-60% by weight of a polyphenylene ether, (b) 0-60% by weight of an alkenyl aromatic resin excluding unhydrogenated alkenyl aromatic block copolymer of tile following component (e) and (c) 40-99% by weight of a polyamide, (d) 1-50 parts by weight of a polyolefin having a modulus of 10000 kg/cm2 or more at room temperature, (e) 1-50 parts by weight of an unhydrogenated alkenyl aromatic block copolymer, and (f) a compatibilizing agent in an amount necessary to improve compatibility of the above components (a) and (c), said (d)-(f) being every 100 parts by weight of (a)-(c), and wherein the thermoplastic resin composition is obtained by melt kneading firstly said (a), (d) and (f) and then secondly said (c) therewith. |