| abstract |
Provided is an abrasion-resistant composition comprising: (I) 100 parts by weight of a polymer component containing: (A) 50-90% by weight, based on the total polymer weight, of a polyolefinic resin having a maximum peak temperature (Tm) of higher than 125 DEG C. as measured by differential scanning calorimetry (DSC); and (B) 10-50% by weight, based on the total polymer weight, of a polyethylenic resin or rubber having a maximum peak temperature (Tm) of lower than 125 DEG C. as measured by DSC; and (II) 30-200 parts by weight of an inorganic flame retardant, said polymer component (I) containing 10-8-10-3 gram equivalent based on 1 g of the polymers, of at least one functional group selected from: a: carboxyl group, an ester group thereof, or an anhydride group thereof, b: epoxy group, c: hydroxyl group, d: amino group, e: alkenyl cyclic imino ether group, and f: silane group. |