| abstract |
A composite article having controlled void volume and mean pore size comprises: (a) polytetrafluoroethylene (PTFE) fibril matrix, and (b) insoluble, non-swellable sorptive particles enmeshed in said matrix, the ratio of non-swellable sorptive particles to PTFE is in the range of 40:1 to 1:4 by weight, the composite article having a porosity in the range of 30 to 80 percent void volume and a mean pore size in the range of 0.3 to 5 micrometers, preferably with at least 90 percent of pores having a size less than 3.6 micrometers. The article is prepared by incorporating lubricant in the precursor admixture in an amount sufficient to exceed the lubricant sorptive capacity of the particles by at least 3 weight percent and up to an amount at which the mass loses its integrity. |