abstract |
A rubber composition obtained by compounding (B) from 0.005 to 50 parts by weight of an polyorganohydrogensiloxane and (C) from 0.00001 to 1 part by weight of a compound of a transition metal belonging to the group VIII with (A) 100 parts by weight of a rubber-forming polymer mainly comprising (I) from 3 to 70% by weight of a polyorganosiloxane represented by the formula: ##EQU1## wherein R represents a substituted or unsubstituted monovalent organic group, 0.02 to 10 mole % of which being a vinyl group; and a represents a number of from 1.900 to 2.004, n and having a degree of polymerization of from 500 to 10,000 and (II) from 30 to 97% by weight of organic rubber, and subjecting the resulting compound to hydrosilylation while effecting shear deformation. The rubber composition is excellent in roll processing properties, mechanical strength, heat resistance, and low-temperature property and is suitable as oil seal and rubber hose. |