| abstract |
Alumina-zirconia composite sintered materials having sufficient high-temperature strength and thermal shock resistance as well as excellent mechanical strength are made by mixing Bayer alumina and/or bauxite as an alumina and baddeleyite and/or zircon sand as a zirconia material in amounts of 50 to 95% by weight of alumina, the balance being zirconia, respectively, subjecting the mixture to heating, melting and quenching, grinding the resulting solid to an average grain size of 10 mu m or smaller, and subjecting the resulting powder to molding and sintering. |