This invention relates to a polychloroprene elastomer distinguished by good processing properties and high tensile strength in the form of a polychloroprene mixture containing a sol polymer and a gel polymer in a ratio, by weight, of from 1:4 to 9:1, characterized in that both polymers have been produced in the presence of from 2.5 to 4.0 parts, by weight, of the potassium salt of disproportionated abietic acid (expressed as acid), from 0.3 to 1.0 part, by weight, of a condensation product of naphthalene sulphonic acid and formaldehyde and from 0.1 to 1.5 parts, by weight, of potassium hydroxide, based in each case on 100 parts, by weight, of monomer, and in that the gel polymer is a copolymer of chloroprene and from 1.5 to 2.5 mole percent, based on total monomer, of a diester corresponding to the following general formula: <IMAGE> wherein R1 and R2 represent hydrogen, chlorine or C1-C4 alkyl; and X represents C2-C10 alkylene. |