| abstract |
A polyethylene terephthalate resin composition capable of providing a molded article of a high crystallinity and an excellent dimensional stability and thermal resistance consists essentially of a polyethylene terephthalate resin having an intrinsic viscosity of 0.35 to 0.9 and, per 100 parts by weight of the polyethylene terephthalate resin, 5 to 200 parts by weight of an inorganic filler, 0.01 to 20 parts by weight of dimethyl or diethyl terephthalate and 0.01 to 5 parts by weight of a salt of a carboxylic acid with a metal of Group I or II in the periodic table or 0.1 to 10 parts by weight of an ionic copolymer of an alpha -olefin with a salt of an alpha , beta -unsaturated carboxylic acid and containing an ion of a metal of Group I or II in the periodic table. |