| abstract |
An interlayer film for laminated glass of the present invention has an average storage modulus (G′) at 110 to 150° C. measured at a frequency of 1 Hz in a shear mode of 15000 Pa or less, and has an adhesive strength of 0.3 N/mm2 or more as measured in a cross peeling test performed under the following conditions on a cross peeling test sample produced by a predetermined method. Cross peeling test: A maximum load (N) when the polycarbonate plate glass is peeled from the clear float plate glass in a direction perpendicular to an adhesive surface at a rate of 10 mm/min at 23° C. is measured, and that measured maximum load (N) is taken as the adhesive strength. |