| abstract |
Provided is an aromatic polycarbonate resin composition, including, with respect to 100 parts by mass of an aromatic polycarbonate resin (A), 0.01 part by mass to 0.1 part by mass of an alicyclic epoxy compound (B), 0.2 part by mass to 0.6 part by mass of a polyether compound (C) having a polyoxyalkylene structure, and 0.005 part by mass to 1 part by mass of a phosphorus-based compound (D), wherein a difference between a YI value of a 5-millimeter thick molded body, which is obtained by molding the aromatic polycarbonate resin composition at 320° C., after a lapse of 3,000 hours under an environment at 85° C. and a humidity of 85%, and an initial YI value thereof is 3.0 or less. |