abstract |
In a method for producing an expanded-glass granular material, starting materials containing glass powder, water glass, at least one blowing agent, and metakaolin, are mixed in order to form a homogeneous slurry. The slurry is granulated to form raw granular-material particles, which are foamed at a baking temperature between 780° C. and 950° C. in order to form expanded-glass granular-material particles. The expanded-glass granular material has a long-term water absorption of less than 25 volume percent when the expanded-glass granular material is exposed to water for a time period of 21 days. |