| abstract |
Disclosed is a high-strength copolymerized aramid fiber which includes aramid copolymers containing an aromatic group substituted with a cyano group (—CN), so as to have an intrinsic viscosity (IV) of 6.0 to 8.5, a polydispersity index (PDI) of 1.5 to 2.0, a strength of 23 to 32 g/d, and an elastic modulus of 1,100 to 1,300 g/d. The high-strength copolymerized aramid fiber may be prepared by a method which includes, when para-phenylenediamine, cyano-para-phenylenediamine, and terephthaloyl dichloride are sequentially added to an organic solvent and reacted together to prepare a copolymerized aramid fiber, adding and dispersing a neutralizing agent in the organic solvent before the reaction of the para-phenylenediamine, cyano-para-phenylenediamine and terephthaloyl dichloride, which were dissolved in the organic solvent. |