| abstract |
Disclosed herein is a method for manufacturing oxide fuel pellets. The method for manufacturing the oxide fuel pellets includes (step 1) preparing nuclear fuel powder containing uranium dioxide (UO2+x, x=0 to 0.20), (step 2) compacting the nuclear fuel powder prepared in step 1 to manufacture green pellets, sintering the green pellets manufactured in step 2 at a temperature of about 1,200° C. to about 1,400° C. by using an atmosphere gas, and reducing the green pellets sintered in step 3 at a temperature of about 800° C. to about 1,000° C. by using a reducing atmosphere gas. The method for manufacturing the oxide fuel pellets according to the present invention performs the sintering at a low temperature of about 1,200° C. to 1,400° C. to manufacture economical and safe oxide fuel pellets that are adequate for the nuclear fuel specification. |