A process for preparing a magnetic talcous composition including mineral particles, referred to as magnetic talcous particles, having a non-zero magnetic susceptibility, in which, during an oxidative contacting step, talcous particles chosen from the group formed from 2:1 lamellar silicates having a zero electric charge are brought into contact with particles including at least one magnetic iron oxide chosen from the group formed from magnetite and maghemite, the magnetic particles having a mean equivalent diameter of between 1 nm and 50 nm. A magnetic talcous composition including mineral particles, referred to as magnetic talcous particles, having a non-zero magnetic susceptibility, at least 20% by weight of talcous particles and at least 0.5% by weight of magnetic particles is also described. |