| abstract |
The invention relates to the method of preparation of hyaluronic acid-based fibres, where first the spinning solution of hyaluronic acid and/or a metal compound thereof, optionally containing a metal salt or a hyaluronic acid compound and metal ions, is prepared, then the spinning solution is introduced into the coagulation bath comprising an acid, an alcohol and not more than 10% wt. of water, and optionally a metal salt, resulting in forming a fibre which is preferably left in the coagulation bath and/or is drawn, then the fibre is washed with alcohol and dried. After washing of the fibre, metal ions may be introduced in the fibre by means of the metalization bath. Further, the invention relates to the fibres based on hyaluronic acid and/or a metal compound thereof, having the fibre (monofilament) diameter 4 μm to 1 mm, linear weight 0.1 to 30 g/1000 m (0.1 to 30 tex), tensile strength 0.5 to 3 cN·dtex −1 and loop strength 20 to 80% of the tensile strength. The invention also relates to a silk tow that contains 2 to 50 primary fibres. Moreover, the invention relates to the use of the fibres for the production of woven and non-swoven fabrics. |