| abstract |
The invention relates to a granulated powder intended, in particular, for the production of ceramic sintered parts, said powder having the following chemical weight composition, based on dry matter, namely: at least 1% of a first binder having a glass transition temperature less than or equal to 25° C.; 0-4% of an additional binder having a glass transition temperature greater than 25° C.; 0-4% of a temporary additive different from the first binder and the additional binder, the total content of the first binder, the additional binder and the temporary additive being less than 9%; 0-15% of an additive for sintering the ceramic material; at least 2% impurities; and the remainder comprising a ceramic material, and optionally an agent for stabilising said ceramic material, to make up 100%. According to the invention, the median diameter D 50 of the powder is between 80 and 130 μm, the percentile D 99.5 is less than 500 gm and the relative density of the granules is between 30% and 60%. |