| abstract |
A process for preparing a slurry catalyst is provided. The slurry catalyst is prepared from at least a Group VIB metal precursor and optionally at least a Promoter metal precursor selected from Group VIII, Group IIB, Group IIA, Group IVA metals and combinations thereof. The slurry catalyst comprises a plurality of dispersed particles in a hydrocarbon medium having an average particle size ranging from 1 to 300 nm. The slurry catalyst is then mixed with a hydrogen feed at a pressure from 1435 psig (10 MPa) to 3610 psig (25 MPa) and a temperature from 200-800° F. at 500 to 15,000 scf hydrogen per bbl of slurry catalyst for a minute to 20 hours, for the slurry catalyst to be saturated with hydrogen providing an increase of k-values in terms of HDS, HDN, and HDMCR of at least 15% compared to a slurry catalyst that is not saturated with hydrogen. |