| abstract |
The catalyst for oxidative dehydrogenation of propane to propylene includes vanadium and aluminum incorporated into the framework of a mesoporous support, viz., MCM-41, to form V—Al-MCM-41, and nickel impregnated onto the walls of the mesoporous support. Nickel loading is preferably in the range of 5 to 15% by weight of the catalyst. A process for the production of propylene from propane includes steps of placing the catalyst in a fixed bed reactor, introducing a flow of feedstock in a propane:oxygen:nitrogen ratio of about 6:6:88 by volume, maintaining the reactor at atmospheric pressure and in a temperature range of about 400 to 550° C., collecting the product, and separating propylene from the product. The process achieves propane conversion between about 6 to 22%, and a selectivity for propylene between about 22 and 70%, depending upon percent nickel content and temperature of the reaction. |