| abstract |
A silver oxide powder that replaces silver powder as a silver conductive paste filler has a specific surface area measured by the BET method is 1.0-25.0 m 2 /g, average primary particle diameter is 1-50 nm, and average secondary particle diameter is 1-1000 nm. The silver oxide powder is made by preparing a neutralization medium that is an aqueous solution containing one or both of sodium hydroxide and potassium hydroxide in a total amount of 0.5 mole/L or less, simultaneously adding an aqueous solution containing silver salt in an amount of 6.0 mole/L or less and an aqueous solution of at least one of sodium hydroxide and potassium hydroxide to the liquid medium to conduct a neutralization reaction, thereby obtaining a neutralized precipitate, maintaining the liquid at a pH in the range of 12±1.5 during the reaction, and subjecting the precipitate to filtration, washing, and drying. |