| abstract |
The invention concerns a micro-composite polymer/polymer material comprising an amorphous polymer (I) forming a dispersed phase localised inside a thermoplastic or elastomeric polymer (II) forming a matrix, the glass transition temperature of polymer (I) forming a dispersed phase being higher by at least 20° C. than the melting or softening point of matrix-forming polymer (II), and the amorphous polymer content (I) forming the dispersed phase being not less than 40 wt. %. The invention also concerns a method for obtaining said material comprising steps which consist in: extruding, at regulated temperature, said melted polymer mixture, said regulating temperature being decreasing from the feeding zone (A) to the die zone (F) of said extruding machine ( 1 ) so that the material temperature in said die zone (F) is lower than the temperature of recrystallisation or solidification of polymer (II), and higher than the melting or softening point of amorphous polymer (I); and cooling at room temperature the resulting micro-composite material. |