| abstract |
Polyimides having a desired combination of high thermo-oxidative stability, low moisture absorption and excellent chemical and corrosion resistance are prepared by reacting a mixture of compounds including (a) 3,3′,4,4′-benzophenonetetracarboxylic dianhydride (BTDA), (b) 3,4′-oxydianiline (3,4′-ODA), and (c) 5-norbornene-2,3-dicarboxylic anhydride (NA) in a high boiling, aprotic solvent to give 5 to 35 % by weight of polyamic acid solution. The ratio of (a), (b), and (c) is selected to afford a family of polyimides having different molecular weights and properties. The mixture first forms a polyamic acid precursor. Upon heating at or above 300° C., the polyamic acids form polyimides, which are particularly suitable for use as a high temperature coating, adhesive, thin film, or composite matrix resin. |