| abstract |
A duplex stainless steel and method of manufacturing the same, said steel having an amount of Cr in an extraction residue [Cr] of 0.005 to 0.050% and an amount of Nb in an extraction residue [Nb] of 0.001 to 0.080%, the [Nb]/[Cr] ratio being 0.2 or more. By slow cooling down to 800° C., then fast cooling down to 600° C., it is possible to control the precipitation of chromium nitrides and niobium nitrides, and by making the ratio [Nb]/[Cr] 0.2 or more, it is possible to raise the corrosion resistance. Further, by reducing Mn to less than 2.0% and N to 0.25% or less, then adding a trace amount of Nb, the effect of raising the critical pitting temperature CPT is obtained. |