| abstract |
It is provided that a method for producing a biaxially oriented polyester film that can be used for industrial and packaging applications. A method for producing a biaxially oriented polyester film, comprising: a step of feeding a polyester resin into an extruder, a step of extruding the molten polyester resin from an extruder to obtain a molten resin sheet at 250 to 310° C., a step of attaching the molten resin sheet closely to a cooling roll by an electrostatic application method to obtain an unstretched sheet, and a step of biaxially stretching the unstretched sheet, wherein the polyester resin fulfills the following (A) to (C): (A) the polyester resin comprises a polyethylene furandicarboxylate resin composed of a furandicarboxylic acid and ethylene glycol; (B) an intrinsic viscosity of the polyester resin is 0.50 dL/g or more; (C) a melt specific resistance value at 250° C. of the polyester resin is 3.0×107 Ω·cm or less. |