| abstract |
A cemented carbide comprises a first hard phase comprising tungsten carbide particles and a binder phase including Co and Cr. In any surface or any cross section of the cemented carbide, a region in which there is a distance X of 5 nm or less between surfaces respectively of tungsten carbide particles adjacent to each other, with the surfaces facing each other along a length L of 100 nm or more, is referred to as a WC/WC interface, and a ratio C(R)/C(C) has an average value of 0.17 or more, where C(R) and C(C) represent peak values of atomic percentages of Cr and Co, respectively, at a WC/WC interface having a distance X of 1 nm or more and 5 nm or less and having therein an atomic percentage of Co higher than an average value of atomic percentages of Co in the tungsten carbide particles+2 at %. |