abstract |
A method for manufacturing a carbon dioxide adsorbent includes preparing an amine aqueous solution having an amine compound concentration ranging from 5% to 70% inclusive and a temperature ranging from 10° C. to 100° C. inclusive, impregnating silica gel with the amine aqueous solution, and aeration-drying the silica gel carrying the amine compound. The silica gel has a particle size ranging from 1 mm to 5 mm inclusive, an average pore diameter ranging from 10 nm to 100 nm inclusive, and a pore volume ranging from 0.1 cm3/g to 1.3 cm3/g inclusive. |