| abstract |
A flame retardant resin composition comprises a polyolefin resin, calcium carbonate particles blended at a ratio of 5 pts. mass to 80 pts. mass, aluminum hydroxide blended at a ratio of 50 pts. mass to 125 pts. mass, a silicone-based compound blended at a ratio of more than 1 pt. mass and 10 pts. mass or less, a fatty acid-containing compound blended at a ratio of 3 pts. mass to 20 pts. mass, and a zinc-containing inorganic compound blended at a ratio of 1 pt. mass to 7 pts. mass, all relative to 100 pts. mass of the polyolefin resin. In the flame retardant resin composition, the calcium carbonate particles and the aluminum hydroxide are blended in total at a ratio of 55 pts. mass to 130 pts. mass relative to 100 pts. mass of the polyolefin resin. |