| abstract |
The present invention provides a resin comprising a polycarbonate resin and a flat cross-section glass fiber, which is excellent in weld seam strength, rigidity, and flame retardancy.nThe glass fiber reinforced polycarbonate resin composition of the present invention is (A) a polycarbonate-polydiorganotoxime copolymerized resin (component A-1) and an aromatic polycarbonate resin (A-2) 100 parts by weight of the resin component (component A) obtained by the component), the average length of the (B) fiber cross section is 10 to 50 μm, and the ratio of the major axis to the minor axis (long diameter/short diameter) is 1.5. ~8 flat cross-section glass fiber (component B) 10 to 300 parts by weight, (C) adhesion improver (component C) 5 to 25 parts by weight, (D) phosphorus-based flame retardant (component D) 5 to 45 The content of the polyfluorinated dripping agent (E component) is 0.01 to 3 parts by weight, and the content of the polydiorganosiloxane derived from the component A-1 in the resin composition is 0.05 to 4.00% by weight. |