| abstract |
A method of coating glass by contacting a gaseous composition comprising a composition comprising a tin oxide precursor such as monobutyltin trichloride, a silica precursor such as tetraethylorthosilicate and an accelerator such as triethyl phosphite, the composition being gaseous at a temperature below 200 ° C and allowing coating. with a temperature in the range of 450 ° C to 650 ° C with a deposition rate greater than 35.0 nm / second. This layer of applied material can be combined with other layers to form a product with specific properties, such as controlled emissivity, refractive index, abrasion resistance and appearance. |