| abstract |
Disclosed are a polyethylene resin composition for artificial turf having excellent soft characteristics and excellent abrasion resistance, and artificial turf prepared therefrom. The present invention (A) has a density of 0.915 to 0.930 g/cm 3 and a melt index (ASTM D1238, 190°C, 2.16 kg) of 0.2 to 10.0 g/10min, and 50 to 89% by weight of linear low density polyethylene manufactured by Ziegler-Natta catalyst ; (B) a density of 0.910 to 0.925 g/cm 3 and a melt index (ASTM D1238, 190°C, 2.16 kg) of 0.2 to 10.0 g/10min, and 10 to 49% by weight of a linear low density polyethylene prepared with a metallocene catalyst; And (C) 1 to 20% by weight of a polyolefin elastomer having a density of 0.850 to 0.910 g/cm 3 and a melt index (ASTM D1238, 190°C, 2.16 kg) of 0.2 to 3.0 g/10min; The composition is provided. |