| abstract |
A binder resin and an inorganic particle dispersion paste for an inorganic particle dispersion paste excellent in both printing property and adhesive property are provided. Wherein the polyvinyl acetal and the cellulose derivative are mixed so as to satisfy a relationship of 0.2? X / (X + Y)? 0.8 when the polyvinyl acetal and the cellulose derivative are respectively referred to as X mass parts and Y mass parts, Spherical nickel particles having an average particle diameter of 0.3 탆, barium titanate particles having an average particle diameter of 0.05 탆, nonionic surface active agents, dihydroterpineol and mineral spirit were mixed and kneaded at a predetermined mixing ratio to obtain a paste, The value of the phase difference delta between the respective strains and the stress caused by the strains when the strains 0.02 and 0.2 were applied at an angular frequency of 6.284 rad / s was greater than 45 degrees, and the shear rate 40 (1 / s ) Is 4.5 or less at a shear rate of 4 (1 / s). |