| abstract |
The present invention provides a method of producing a hard coat film having a hard coat formed on at least one side of a film substrate with an active energy ray curable resin composition, wherein the active energy ray curable resin composition comprises (P) a urethane (meth) (Q) 0.02-5 parts by mass of organic fine particles having an average particle size of 10-300 nm and (R) 0.0002-2 parts by mass of an acrylic silicone leveling agent, the method comprising: (1) (2) a step of drying the wet coating film to form a dried coating film; (3) a step of drying the wet coating film at a temperature of 50 to 90 DEG C , And irradiating an active energy ray to cure the film to form a hard coat film. |