| abstract |
The present invention is a thermoplastic polyester and 100 parts by weight (I) of the hard component, 0 to 300 parts by weight of filler (II), 1 to 10 parts by weight of vulcanizing agent (III), 0 to 4 parts by weight of vulcanization activator (IV) And a composite product prepared from vulcanized rubber, which is a soft component prepared by vulcanizing a rubber composition comprising 0 to 150 parts by weight of a plasticizer in contact with a hard component under ordinary vulcanization conditions, wherein (a) Optionally, the hard and / or soft component further comprises 0.5-12 parts by weight of a mixture of two or more di- or polyfunctional maleimides of Formula 1, and (b) the hard component comprises a bi- or polyfunctional maleimide. Rubber, if not included, having a carboxyl or anhydride group] and a process for the preparation thereof, wherein the unsubstituted maleimide at the double bond carbon position and the horse substituted at the double bond carbon position It will already have about how to use the de together.n n n The method of the present invention provides a robust composite product. |